1. What is Electroplating?

Electroplating is a process commonly known as Electrolysis. Electrolysis producing a chemical change by passing an electrical current through to the electrolyte (solution). The ions migrating to the electrodes, the positive ions which are the metal being deposited are attracted to the negatively charged electrode (the part being plated). The negative ions are attracted to the positive electrode (Anode) and given off as gases.

2. What is Brush Plating?

The theory of brush plating is very basic. The part to be plated is given a negative (-) charge through a flexible wire lead from a special D.C. power pack. The plating tool or “brush” is positively ( ) charged from the same power pack by a second insulated flexible lead. The plating tool assembly consists of an insulated handle with a graphite or stainless steel anode. The anode is covered with an absorbent material such as Dacron felt. The plating tool is then dipped into the desired plating solution and rubbed over the area where the coating is desired the plating only takes place where the anode contacts the part. The operator must maintain movement between the anode and the part to ensure sound metal deposits.

3. Applications.

Navy & Marine, Aircraft & Aerospace Industries, Printing Industries, Electrical & Electronic Industry and General Engineering including Mould and Die making.

4. What advantages does Brush Plating have?

Portability, Ease of operation, Rapid metal build up, Disassemble of machines, Plating of larger parts that won’t fit in a tank, Excellent Adhesion, Dense coatings, No thermal distortion, Minimize hydrogen Embrittlement and reduces waste.

5. What disadvantages does Brush Plating have?

Difficulty in plating complex shapes. In most cases, only one part at a time and it is a very labour intensive operation.

6. What is the meaning of Selective Plating?

Selective plating means that you can selectively plate an area by the means of masking off areas that need not be plated with either masking tapes or masking paints. Just like painting the material on. The job becomes the canvas or Cathode and the brush is the Anode and the paint is the metal.

7. Does Brush Plating the same approvals as tank plating?

Brush plating is approved to many standards. Brush plating has many of its own approvals and these can be supplied from Sifco on request.  Many marine, electrical, aircraft and military bodies approve brush plating.

8. Is it permanent?

Yes, Selective Plating is exactly the same as tank plating but much faster to lay down and has bond strength as good as the base metal if the process is used correctly.

9. How thick can you Plate?

Thickness is no problem but the costs are. In brush plating, any thickness can be achieved by plating until the recommended thickness by Sifco solution data sheets is achieved then the area must be smoothed off and reactivated and plating carried out again. With harder materials, it is common practice to lay a sandwich layer (i.e. Copper base with a hard nickel cap) this is far the cheapest way to lay a heavy thickness.

10. Can ID & OD areas be plated as well as flat areas?

Yes, all areas can be plated with the LDC Selective brush plating. Spun bearings are a common repair on Shafts or Gear Box housings and are ideally suited to brush plating. Using some type of turning head or lathe to rotate the shaft or spindle or using an ID plater unit to plate Gearbox ID’s.

11. Can tank-plating solutions be used for brush plating?

No. The content of brush plating solutions have a much higher content of metal than tank plating. If tank-plating solutions were used then a powdery deposit would be achieved.

12. Can Brush plating be done anywhere?

Yes, this is called IN SITUE PLATING. The equipment can be transported anywhere. The metal is in the solution and the only other item needed is single-phase electricity. If larger deposits are needed then 3-phase power is needed and some kind of mechanical finishing might be necessary.

13. Can a Hard Chrome deposit be plated?

Sifco chrome. The problem is that it takes a long time to lay down approximately 10 times longer than nickel and is expensive in both time and material. Hard chrome can be plated with other materials if needed such as Nickel Cobalt.

14.  Can threads be plated?

This is called anti-gailing. Brush plating can be used for this purpose but it must be stressed, the throwing power must be considered on each application. Copper is the most commonly used material.

15. Can all metal materials be plated on?

Most materials can be plated on as long as they are not a base material such as steel and stainless steel. Base materials can be plated on but not plated. Sifco has nearly a hundred solutions and a good selection of each material.

16. Can brush-plating materials be plated on two or more Base Metals?

Yes, unlike tank plating brush plating has the capability of plating on two base metals because of the activating processes that can be changed to suit different materials.

17. What hardness can be achieved with brush plating?

This depends on the solution being used. Sifco has hard chrome that is approx 70 Rockwell, Nickels at 48, 54 Rockwell, and Rhodium at 64 Rockwell and Nickel tungsten at 58 Rockwell.

18. Has Sifco any Wear Resistant Materials.

Sifco has a number of good wear resident materials. Chrome, Nickel, Nickel Cobalt, Cobalt-Tungsten, Nickel Tungsten, Rhodium. Etc

19. Is brush plating used for corrosion protection?

Many of the brush plating solutions and applications are used for corrosion protection. The main material is Nickel, Copper, Zinc, Tin and Cadmium

20. Does brush plating cause hydrogen embrittlement?

The Sifco brush plating procedures have been approved by aircraft manufacturers to stop hydrogen embrittlement and Sifco has manufactured solutions that will not cause this such as cadmium NO-Bake. Cadmium LHE 5070 and Zinc Nickel LHE 5970

21. Can you brush plate on Aluminum?

Yes, brush-plating solutions are used very much for this purpose mostly with nickel for better soldering and brazing.

22. Can you brush plate to a certain thickness?

Yes, brush-plating can be worked out to plate a certain thickness and the power packs can be set to turn off all plating at that time.

23. Are there any high-temperature materials?

A number of the solutions can be used in the high-temperature range Chrome 1888c, Cobalt 1493c, Nickels 1454c, Palladium 1552c, and Coppers 1082c.

24. Can hydraulic rams or spears be repaired with brush plating?

Hydraulic rams are a big part of the brush plating service because the plating can be brought to the ram rather than the ram going to the platers. Hard Chrome or nickel and nickel cobalt are used for this purpose after the damage has been filled with copper.

25. If Rams can be repaired then can Print Cylinders be repaired in situ?

Yes, again this is a big part the service provided by brush platers. The same process as hydraulic rams this saves many hours of downtime for the printing companies.

26. Do you have to Finish Brush Plating after plating has been carried out?

This depends on the finish required. If a large amount of plating is carried out then finishing will be required. If a very small amount of plating is laid down and the previous surface is good then no finishing is required.

27. What kind of finishing can be carried out after plating has been carried out?

This depends on the material used. Copper and soft materials like tin can be machined easily on lathes Etc. Nickel and Nickel based materials need to be ground using plenty of coolant. On some occasions a copper base is put down machined on lathes Etc. and a hard capping is put over the top. This is called a sandwich coating. Some bearing retainer diameters need not have capping as the copper is as hard on compression as the base material EG Mild Steel. Print cylinder and Hydraulic repair is usually finished by hand.

28. Are there any white metal bearing solutions?

The white metal solution is called Babbitt and is an excellent bearing material mainly used on aircraft.

29. Can needle-bearing diameters be plated?

Needle bearing diameters can be plated but is a very hard process and much care must be taken. Nickel Cobalt is a very dense material and is suitable for this application.

30.  Can bearing diameters be plated in copper and then capped?

Yes, copper is as hard as steel on compression up to 65000 tons per sq inch so capping is not necessary but for visual and cosmetic purposes it can be done.

31. What advantages does Brush Plating have over welding

Both welding and Brush plating have their advantages. Brush plating has one very good advantage is that no heat at all is needed. The solution heats itself sometimes and some solutions need heating for better density and adhesion but you can always place your hand on the item being plated.

32.  Are there any safety issues in using Sifco Solutions?

All Sifco operators are trained at special training centres and should know the safety procedures needed to carry out plating. Some of the solutions are acid based so precautions must be observed.

33.  Can an unknown base material be found with LDC Solutions?

Yes, by using solutions –no2 Etch or No. 4 Etch in Reverse, then by looking in the wrap material a colour will be observed. A magnetic test can also be carried out as well.

34. Can anybody carry out Brush Plating?

NO. All Sifco operators are trained at special training centres and know how calculations and laid down procedures are carried out. At the end of all training classes test are conducted and only passes will be given operators certificates. If un-trained operators try this process then failures will occur.

35.  Have Sifco Solutions got a shelf life?

Yes, Some of the solutions have like Babbitt, Cad Coat, Tin Nickel and Nickel Zinc. The other solutions have been tested and have shown no deterioration after five years.

36. Are special Anode Wraps required?

Yes, Special wraps are required for special solutions. But the most common wrap used is a red Scotchbrite that tends to keep the surface clean as its plating.

37.  Why use Copper as a defect repair filler and is it hard enough.

Copper is used as a filler because it is always overstated about the yield strength needed for compression. If you take copper filling solutions Brinell hardness of approx 134 times this by 500 and you will get Compressive Yield Strength (PSI) so this example gives a 67000 PSI.

“O” ring seal strength is approx 2000 PSI. Many of the brush plating solutions and applications are used for corrosion protection. The main material is Nickel, Copper, Zinc, Tin and Cadmium